涂布无铬钝化剂和防锈油的镀锌铝镁板局部腐蚀原因分析

展开
  • 1.鞍钢集团钢铁研究院,辽宁 鞍山 114009; 2.辽宁科技大学化工学院,辽宁 鞍山 114051
姜效军(1961-),教授,博导,研究方向为金属腐蚀与防护,E-mail:anshanjiangxj@163.com

收稿日期: 2022-09-16

  修回日期: 2022-10-12

  录用日期: 2022-11-17

  网络出版日期: 2023-03-15

基金资助

国家重点研发专项基金(2017YFB0304305)资助

Analysis on Localized Corrosion Causes of Galvanized Al-Mg Steel Plate Coated with Chromium Free Passivator and Antirust Oil

Expand
  • 1.Iron and Steel Research Institute of Ansteel Group,Anshan 114009,China; 2.School of Chemical Engineering,University of Science and Technology Liaoning,Anshan 114051,China

Received date: 2022-09-16

  Revised date: 2022-10-12

  Accepted date: 2022-11-17

  Online published: 2023-03-15

摘要

为探索镀锌铝镁板在涂覆无铬钝化液和防锈油后在运输环境下的腐蚀机理,利用XPS 和能谱技术分析了色差区的元素差异;利用原子力显微镜考察了镀锌板无铬钝化膜腐蚀前后的微观结构;利用Raman 光谱分析了涂布无铬钝化剂的固化机理及防护过程。研究得出:防锈油组分与钝化膜组分反应影响了涂覆膜的防锈性能;Raman 光谱揭示提高固化板温到90 ℃固化更完全,防锈能力明显增强。

本文引用格式

徐闻慧, 杨洪刚, 吕家舜, 金勇, 姜效军 . 涂布无铬钝化剂和防锈油的镀锌铝镁板局部腐蚀原因分析[J]. 材料保护, 2023 , 56(3) : 183 -188 . DOI: 10.16577/j.issn.1001-1560.2023.0076

Abstract

In order to explore the corrosion mechanism of galvanized Al-Mg steel plate coated with chromium-free passive solution and anti-rust oil in the transportation environment,XPS and EDS were used to analyze the element differences in the color-difference zone.The microstructure of chromium-free passive film of the galvanized sheet before and after corrosion was investigated by atomic force microscope.Raman spectroscopy was used to analyze the curing mechanism and protection process of coated chromium-free passivator.Results showed that the reaction between the components of antirust oil and passive film affected the antirust performance of the coating film.Raman spectrum revealed that the cured plate could be cured more completely by increasing the temperature to 90 ℃,and the anti-rust ability was obviously enhanced.

参考文献

[1] 杜 昕,张满仓,段朝学,等.耐腐蚀锌铝镁镀层研究现状[J].工程科学学报,2019,41(7):847-856.DU X,ZHANG M C,DUAN C X,et al.Chinese Journal of Engineering,Research status of high corrosion-resistant Zn-Al-Mg coating,2019,41(7):847-856.

[2] 郝玉林,生 海,赵 一.锌铝镁在NaCl 中腐蚀行为研究[J].涂料工业,2018,48(12):7-15.HAO Y L,SHENG H,ZHAO Y.Study on Corrosion Behavior of Zn-Al-Mg Coating in 3.5%NaCl Solution[J].Paint &Coatings Industry,2018,48(12):7-15.

[3] 明振涛.热浸镀彩涂板腐蚀失效分析及耐蚀性能对比研究[D].杭州:浙江工业大学,2018: 66-69.MING Z T.Study on Failure Behavior and Corrosion Resistance Comparision of Hot-Dip Prepaainted Sheet[D].Hangzhou: Zhejiang Univerity of Technology,2018: 66-69.

[4] ZHANG G B,WANG Y S,ZHANG S N,et al.Corrosion Failure Analysis of Hot-Dip Galvanized Steel in a Room Environment [J].Journal of Failure Analysis and Prevention,2015,15(6):868-872.

[5] JAIYEOLA G A.Microbiologically Influenced Corrosion of Galvanized Steel by a Metalworking Lube[J].Journal of Failure Analysis and Prevention,2013,13(2):136-139.[6] PISTOFIDIS N,VOURLIAS G,STERGIOUDIS G.Shortterm corrosion behavior of galvanized coatings in natural waters of the Greek territory[J].Journal of Materials Science,2007,42(8): 2 879-2 885.

[7] WANG L,LIU C S,YU H Y.Structure and Corrosion Resistance of a Composite γ-Amino Propyl Triethoxy Silane and γ-Glycidoxy Propyl Trimethoxy Silane Conversion Coating on Galvanized Steel[J].Journal of Iron and Steel Research International,2012,19(11): 46-51.

[8] YU S P,TAI H J.Sol-gel enhanced polyurethane coating for corrosion protection of 55% Al-Zn alloy-coated steel[J].Journal of Polymer Research,2021,28(158):3-11.

[9] BARTON K,CULLEN M,DUFFY B.Sol-Gel Chemistry Engineering for Corrosion Protection,Sol-Gel Materials for Energy[J].Environment and Electronic Applications,2017(2): 197-241.

[10] VUORI L,Ali-Löytty H,LAHTONEN K,et al.Improved Corrosion Properties of Hot Dip Galvanized Steel by Nanomolecular Silane Layers as Hybrid Interface Between Zinc and Top Coatings[J].Corrosion,2017,73(2):169-180.

[11] 吕家舜,杨洪刚,徐闻慧,等.热浸镀锌铝镁钢板环保钝化剂涂层防护机理[J].涂料工业,2022,52(12):14-18.LV J S,YANG H G,XU W H,et al.The mechanism of protection of coating environmental passivation for galvanized aluminum magnesium steel plate[J].Paint & Coatings Industry,2022,52(12):14-18.

文章导航

/