Effect of Electromagnetic Field on the Corrosion Behavior of 2507 Super Duplex Stainless Steel

Expand
  • 1.Anhui Key Laboratory of High Performance Nonferrous Metal Materials,Anhui Polytechnic University,Wuhu 241000,China;2.Key Laboratory of Marine Materials and Related Technologies,Zhejiang Key Laboratory of Marine Materials and Protective Technologies,Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences,Ningbo 315201,China;3.School of Materials Science and Engineering,Kunming University of Science and Technology,Kunming 650093,China;4.School of Opto-Electronic Engineering,Changchun University of Science and Technology,Changchun 130022,China;5.Ningbo Oriental Cable Co.,Ltd.,Ningbo 315801,China

Received date: 2023-02-15

  Revised date: 2023-03-12

  Accepted date: 2023-04-16

  Online published: 2023-08-23

摘要

针对海洋用脐带缆用2507 超级双相不锈钢的电磁场腐蚀行为,利用动电位极化、电化学阻抗谱及Mott-Schottky 分析,研究电磁场变化对2507 超级双相不锈钢在模拟海水中电化学性质的影响;采用SEM 及EDS分析2507 超级双相不锈钢的腐蚀形貌及产物。结果表明:电磁场会促进2507 超级双相不锈钢在3.5%NaCl 溶液中的腐蚀;随着电磁场强度的增加,自腐蚀电位下降,阻抗降低,腐蚀加剧;2507 超级双相不锈钢在3.5%NaCl 溶液中形成的钝化膜半导体产生P-N 转化,励磁电流越大,转化电位越负。

本文引用格式

黄泽政, 唐楚天, 黄仲佳, 毛飞雄, 高慧杰, 陈 凯, 俞国军 . 电磁场对2507 超级双相不锈钢腐蚀行为的影响[J]. 材料保护, 2023 , 56(7) : 64 -69 . DOI: 10.16577/j.issn.1001-1560.2023.0162

Abstract

Aiming at the electromagnetic corrosion behavior of 2507 super duplex stainless steel used for ocean umbilical cable,the effects of electromagnetic field changes on the electrochemical properties of 2507 super duplex stainless steel in simulated seawater were studied by potentiodynamic polarization,electrochemical impedance spectroscopy and Mott Schottky analysis.Subsequently,SEM and EDS were used to analyze the corrosion morphology and products of 2507 super duplex stainless steel.Results showed that the electromagnetic field could promote the corrosion of 2507 super duplex stainless steel in 3.5%NaCl solution.As the intensity of the electromagnetic field increased,self-corrosion potential and the impedance decreased,so the corrosion became more serious.Meanwhile,the passivation film semiconductor formed by 2507 super duplex stainless steel in 3.5%NaCl solution generated P-N conversion,and the higher the excitation current,the more negative the conversion potential.

参考文献

[1] 孙 超,韩术亮,李 勇.海洋石油平台管道布置设计与研究[J].化学工程与装备,2019(4): 41-42.SUN C,HAN S L,LI Y.Design and research on pipeline layout of offshore oil platform[J].Chemical Engineering &Equipment,2019(4): 41-42.

[2] 史 丹,刘佳骏.我国海洋能源开发现状与政策建议[J].中国能源,2013,35(9):6-11.SHI D,LIU J J.Discussion on China's marine energy development situation and policy suggestions[J].Energy of China,2013,35(9):6-11.[3] 邢志光.海上电站多能平台:海洋能源利用的新路径[J].能源,2021(3):70-72.XING Z G.Multi energy platforms for offshore power plants:a new path for ocean energy utilization Energy[J].Energy,2021(3):70-72.

[4] 郭 宏,屈 衍,李 博,等.国内外脐带缆技术研究现状及在我国的应用展望[J].中国海上油气,2012(1):74-78.GUO H,QU Y,LI B,et al.Research situation on domestic and abroad umbilical cord technology and prospect of application in China[J].China Offshore Oil and Gas,2012(1):74-78.

[5] ODHIAMBO J G,ZHANG L,LIU T,et al.Corrosion behaviour of 2205 duplex stainless steel in marine conditions containing Erythrobacter pelagi bacteria [J].Materials Chemistry and Physics,2020,239:122010.[6] XU D,XIA J,ZHOU E,et al.Accelerated corrosion of 2205 duplex stainless steel caused by marine aerobic Pseudomonas aeruginosa biofilm[J].Bioelectrochemistry,2016,113:1-8.

[7] 陈散兴,樊 栋,张三平.磁场对电化学腐蚀行为的影响[J].材料保护,2015,48(9):31-35.CHEN S X,FAN D,ZHANG S P.Influence of magnetic field on electrochemical corrosion behavior[J].Materials Protetion,2015,48(9):31-35.

[8] GHABASHY M E,SEDAHMED G H,MANSOUR I A S.Effect of a Magnetic Field on the Rate of Diffusion-Controlled Corrosion of Metals[J].British Corrosion Journal,1982,17(1):36-37.

[9] 郭 凯,岳增武,李辛庚.架空地线腐蚀与防护技术发展现状[J].山东电力技术,2014(5): 25-29.GUO K,YUE Z W,LI X G.The development of anti-sorrosion technology for overhead ground wires[J].Shandong Electric Power,2014(5): 25-29.

[10] RALPH SUEPTITZ K,TSCHULIK M,UHLEMANN L,et al.Magnetic field effects on the active dissolution of iron[J].Electrochimica Acta,2011,56 (17): 5 866-5 871.

[11] BOTELLO -ZUBIATE M E,ALVAREZ A,Martínez -Villafañe A,et al.Influence of magnetic water treatment on the calcium carbonate phase formation and the electrochemical corrosion behavior of carbon steel[J].Journal of Alloys and Compounds,2004,369(1/2):256-259.

[12] ZHANG P,ZHU Q,SU Q,et al.Corrosion behavior of T2 copper in 3.5% solution treated by rotating electromagnetic field[J].Transactions of Nonferrous Metals Society of China,2016,26(5):1 439-1 446.

[13] 王大成,曹生现,吕昌旗.交流电磁场对几种金属腐蚀行为的影响[J].腐蚀与防护,2018,39(3): 213-217.WANG D C,CAO S X,LV C Q.Effects of AC electromagnetic field on corrosion performance of several metals[J].Corrosion & Protection,2018,39(3): 213-217.

[14] 张 敏,张恩华,孟 强,等.腐蚀介质对双相不锈钢2205 腐蚀性能影响的研究[J].兵器材料科学与工程,2011(6):44-47.ZHANG M,ZHANG E H,MENG Q,et al.Effect of corrosive medium on the corrosion resistance of duplex stainless steel 2205[J].Ordnance Material Science and Engineering,2011(6):44-47.

[15] 韩小康,覃 明,李佳润,等.不锈钢在海水中的腐蚀行为研究进展[J].材料保护,2017,50(9):75-81.HAN X K,QIN M,LI J R,et al.Research progress on corrosion behavior of stainless steel in seawater[J].Materials Protection,2017,50(9): 75-81.

[16] 李慕勤,李俊刚,吕 迎.材料表面工程技术[M].北京:化学工业出版社,2010.LI M Q,LI J G,LV Y.Material Surface Engineering Technology[M].Beijing: Chemical Industry Press,2010.

[17] 曾初升.316L 不锈钢腐蚀性能电化学研究[D].昆明:昆明理工大学,2006.ZENG C S.Electrochemical Study on the Corrosion Performance of 316L Stainless Steel[D].Kunming:Kunming University of Science and Technology,2006.

[18] 程柏璋,屈少鹏,董丽华,等.深海环境中静水压对2205 钢腐蚀电化学行为的影响[J].腐蚀与防护,2018,39(11): 815-819.CHENG B Z,QU S P,DONG L H,et al.Influence of hydrostatic pressure on the corrosion electrochemistry behaviors of 2205 steel in deep sea environment[J].Corrosion & Protection,2018,39(11): 815-819.

[19] 张鸣伦,王 丹,王兴发,等.海水环境中Cl-浓度对316L不锈钢腐蚀行为的影响[J].材料保护,2019,52(1):34-39.ZHANG M L,WANG D,WANG X F,et al.Influence of Cl- concentrations on the corrosion behavior of 316L stainless steel in ocean environment[J].Materials Protection,2019,52(1):34-39.

[20] ZHANG S,LIAN J,GUO Y,et al.The Semiconductor Character and Corrosion Resistance of Passive Film of 316L Stainless Steel (SS) and Nickel Alloy 800 Formed in Zinc Contained High -Temperature and High -Pressure Water:2011 Asia-Pacific Power and Energy Engineering Conference[C].New York:IEEE,2011.

[21] 盛耀权,王兴平,刘子涵,等.不锈钢在酸性氯化物溶液中的腐蚀行为[J].材料保护,2019,52(8):24-29.SHENG Y Q,WANG X P,LIU Z H,et al.Corrosion behavior of stainless steel in acidic chloride solution[J].Materials Protection,2019,52(8):24-29.

[22] FUJIMOTO S,TSUCHIYA H.Semiconductor properties and protective role of passive films of iron base alloys[J].Corrosion Science,2007,49(1):195-202.

[23] LV J L,YANG M,MIURA H,et al.The effect of surface enriched chromium and grain refinement by ball milling on corrosion resistance of 316L stainless steel[J].Materials Research Bulletin,2017,91:91-97.
文章导航

/