Study on High-Temperature Antibonding Performance of Load Bearing Boards Coated with Nano Yttrium Stabilized Zirconia Coating

Expand
  • (1. College of Mechanical Engineering, Donghua University, Shanghai 201620, China;2. Ningbo Sipurui Machinery Remanufacturing Co., Ltd., Ningbo 315311, China;3. Shanghai SHEFEI Surface Science &Technology Co., Ltd., Shanghai 200051, China)

Received date: 2023-06-25

  Revised date: 2023-07-10

  Accepted date: 2023-08-14

  Online published: 2024-01-08

摘要

为了提高陶瓷承烧板的高温防粘结性能,采用等离子喷涂技术在刚玉-莫来石陶瓷基体上制备纳米钇稳定氧化锆涂层(n-YSZ)和常规钇稳定氧化锆(r-YSZ)涂层,对涂层进行表面形貌分析及孔隙率测试,采用高温熔滴黏附试验测试涂层的接触角。结果显示:n-YSZ涂层表面形貌更加平整致密且表面孔隙率更低,有利于阻止熔滴的侵入破坏,与BaTiO3熔滴的平均接触角最大且大于90°,可明显改善承烧板的高温粘结损坏问题,延长承烧板的使用寿命。

本文引用格式

徐志阳, 孔永华, 尹志坚 . 外覆纳米钇稳定氧化锆涂层承烧板的高温防粘结性能研究[J]. 材料保护, 2023 , 56(12) : 44 -49 . DOI: 10.16577/j.issn.1001-1560.2023.0287

Abstract

For improving the high-temperature antibonding performance of ceramic load bearing boards, nano yttrium stabilized zirconia (n-YSZ) coatings and conventional yttrium stabilized zirconia (r-YSZ) coatings were prepared on corundum-mullite ceramic basal plate by plasma spraying technology. In addition, the surface morphology analysis and porosity test of the coating were conducted, and the high-temperature droplet adhesion test was used to evaluate the contact angle of the coating. Results showed that the surface morphology of n-YSZ coating was smoother and denser, and the surface porosity was lower, which was beneficial to preventing the invasion and damage of molten droplets. Moreover, The average contact angle between n-YSZ coating and BaTiO3 droplet was the highest and greater than 90 °, which could significantly improve the high-temperature bonding damage problem of load bearing boards, and extend the service life of load bearing boards.