GH907高温合金在中性盐雾环境下的初期腐蚀行为研究

刘天, 杨国昊, 张露, 孙海静, 孙杰

doi:10.16577/j.issn.1001-1560.2024.0032

材料保护 >

2024 , Vol. 57 >Issue 2: 43 - 50

DOI: https://doi.org/10.16577/j.issn.1001-1560.2024.0032

研究篇

GH907高温合金在中性盐雾环境下的初期腐蚀行为研究

展开

沈阳理工大学环境与化学工程学院

孙杰(1971-)，博士，教授，研究方向为金属的腐蚀与防护，E-mail: jiersun2000＠126.com

收稿日期: 2023-04-03

修回日期: 2023-06-02

录用日期: 2023-06-14

网络出版日期: 2024-03-08

收起

Study on Initial Corrosion Behavior of GH907 Superalloy in Neutral Salt Spray Environment

Expand

(School of Environmental and Chemical Engineering， Shenyang Ligong University， Shenyang 110159， China)

SUN Jie (1971-)，Ph.D.，Professor，Research Focus:Metal Corrosion and Protection，E-mail:jiersun2000＠ 126.com

Received date: 2023-04-03

Revised date: 2023-06-02

Accepted date: 2023-06-14

Online published: 2024-03-08

Fold

摘要

GH907 高温合金在飞机、船舶等行业得到了广泛的应用。 GH907 高温合金在海洋环境中使用时会导致腐蚀的发生，因此对其腐蚀行为进行研究是必要的。使用中性盐雾试验方法，研究了GH907 高温合金材料在模拟海洋环境中的腐蚀行为。通过扫描电镜、X 射线能谱仪(EDS)和3D 激光共聚焦等方法，观察GH907 高温合金腐蚀后的二维、三维形貌并进行了成分分析；通过动电位扫描和电化学阻抗谱的电化学测试，分析其电化学腐蚀行为。结果表明:GH907 材料在中性盐雾腐蚀过程中会发生钝化行为，腐蚀后的GH907 腐蚀电流密度增加，耐蚀性下降，腐蚀产物和钝化膜对材料的保护能力有限。腐蚀类型以点蚀为主，EDS 结果显示点蚀坑内腐蚀产物以Fe 的氧化物为主，Ni、Co 元素含量很低。腐蚀过程中同时存在电荷转移与扩散行为，腐蚀体系为活化控制体系。

关键词： GH907 高温合金; 腐蚀行为; 中性盐雾; 电化学测试

本文引用格式

刘天, 杨国昊, 张露, 孙海静, 孙杰 . GH907高温合金在中性盐雾环境下的初期腐蚀行为研究[J]. 材料保护, 2024 , 57(2) : 43 -50 . DOI: 10.16577/j.issn.1001-1560.2024.0032

Abstract

GH907 superalloy has been widely used in aircraft，ship and other industries.Because GH907 superalloy will be corroded when used in marine environment， it is necessary to study its corrosion behavior.In this work， the corrosion behavior of GH907 superalloy material in simulated marine environment was studied by neutral salt spray test.The 2D and 3D morphology of GH907 superalloy after corrosion were observed by means of scanning electron microscope (SEM)，X-ray energy dispersive spectroscopy (EDS) and 3D confocal laser scanning，and the composition of GH907 superalloy was analyzed.Moreover，the electrochemical corrosion behavior of GH907 superalloy was analyzed through electrochemical tests of potentiodynamic scanning and electrochemical impedance spectroscopy.Results showed that GH907 material would undergo passivation behavior during neutral salt spray corrosion.After corrosion， the corrosion current density of GH907 increased， the corrosion resistance decreased， and the corrosion products and passivation film possessed limited ability to protect the material.Furthermore， the main corrosion type was pitting corrosion.EDS results revealed that the corrosion products in the pitting pits were mainly Fe oxides， with very low Ni and Co element contents.Besides， the charge transfer and diffusion behavior existed in the corrosion process， and the corrosion system was an activation control system.

Key words： GH907 superalloy; corrosion behavior; neutral salt spray; electrochemical test