掺杂氧化钇及氧化铬颗粒对纯铝微弧氧化膜层性能的影响

杨涵, 冯军, 金凡亚, 李必文, 黄熠, 但敏, 翦奉林, 唐国庆

doi:10.16577/j.issn.1001-1560.2023.0082

Email Alert　 RSS

材料保护 >

2023 , Vol. 56 >Issue 4: 46 - 53

DOI: https://doi.org/10.16577/j.issn.1001-1560.2023.0082

试验研究

掺杂氧化钇及氧化铬颗粒对纯铝微弧氧化膜层性能的影响

展开

¹南华大学机械工程学院； ²核工业西南物理研究院

冯军(1979-)，博士，副教授，研究方向为低温等离子应用，电话:15096080669，E-mail:speedfjkang＠163.com；

金凡亚(1978-)，博士，研究员，研究方向为等离子体应用，电话:028-82820933，E-mail:yafanjin＠163.com

收稿日期: 2022-10-23

修回日期: 2022-11-12

录用日期: 2022-12-14

网络出版日期: 2023-08-03

基金资助

国家磁约束核聚变能发展研究专项(2018YFE0313100)资助

收起

Effect of Doping Yttrium Oxide and Chromium Oxide Particles on the Properties of Pure Aluminum Micro-Arc Oxidation Film

Expand

(1.School of Mechanical Engineering，University of South China，Hengyang 421000，China；2.Southwest Institute of Physics of Nuclear Industry，Chengdu 610041，China)

Received date: 2022-10-23

Revised date: 2022-11-12

Accepted date: 2022-12-14

Online published: 2023-08-03

Fold

摘要

为了探究氧化钇和氧化铬颗粒对纯铝微弧氧化膜层性能的影响,采用磷酸盐电解液体系,以氧化钇和氧化铬为添加剂,利用微弧氧化技术,在1060工业纯铝表面制备微弧氧化膜层。利用扫描电镜(SEM)、X射线衍射仪器(XRD)、涡流测厚仪、显微硬度计、台阶仪器、摩擦磨损试验机和电化学方法分析测试了膜层的表面形貌、相组成、厚度、硬度、粗糙度、耐磨损性能和耐腐蚀性能。结果表明:与单独添加2.5 g/L Y2O3和2.5 g/L Cr2O3条件下相比,在电解液中同时加入2.5 g/L Y2O3和2.5 g/L Cr2O3制备的复合膜层表面孔洞数量减少,表面更加致密,耐磨性较好,膜层的显微硬度达到746 HV、厚度达到20.1μm、粗糙度达到2226.2 nm,且此时的复合膜层的自腐蚀电位最大,自腐蚀电流密度最小,耐腐蚀性能最好。

关键词： 铝; 微弧氧化; 氧化铬; 氧化钇; 耐磨损; 耐腐蚀性

本文引用格式

杨涵, 冯军, 金凡亚, 李必文, 黄熠, 但敏, 翦奉林, 唐国庆 . 掺杂氧化钇及氧化铬颗粒对纯铝微弧氧化膜层性能的影响[J]. 材料保护, 2023 , 56(4) : 46 -53 . DOI: 10.16577/j.issn.1001-1560.2023.0082

Abstract

For exploring the effects of yttrium oxide and chromium oxide particles on the properties of pure aluminum micro-arc oxide films，micro-arc oxide films were prepared on the surface of 1060 industrial pure aluminum by micro-arc oxidation technology in the phosphateelectrolytic liquid system with yttrium oxide and chromium oxide as additives.Scanning electron microscopy (SEM)，X-ray diffraction (XRD)instrument，eddy current thickness meter，microhardness meter，step profiler，friction and wear testing machine，and electrochemical method were employed to characterize the surface morphology，phase composition，thickness，hardness，roughness，wear resistance and corrosion resistance.Results showed that compared with the film prepared with the addition of 2.5 g/L Y2O3 or 2.5 g/L Cr2O3 alone，the composite film prepared by adding 2.5g/L Y2O3 and 2.5g/L Cr2O3 possessed fewer holes on the surface，more compact surface and better wear resistance，with a microhardness of 746 HV，a thickness of 20.1 μm and a roughness of 2 226.2 nm.Meanwhile，the composite film had the maximum self-corrosion potential，the minimum self-corrosion current density and the optimal corrosion resistance.

Key words： aluminum; micro-arc oxidation; Cr₂O₃; Y₂O₃; wear resistance; corrosion resistance