渗氢X70管线钢焊接接头的力学性能及缺口敏感性

陈烨, 王万里, 占先强, 刘俊建, 汤文明

doi:10.16577/j.issn.1001-1560.2024.0197

材料保护 >

2024 , Vol. 57 >Issue 9: 20 - 27

DOI: https://doi.org/10.16577/j.issn.1001-1560.2024.0197

研究篇

渗氢X70管线钢焊接接头的力学性能及缺口敏感性

展开

¹合肥工业大学材料科学与工程学院； ²大唐锅炉压力容器检测中心有限公司； ³大唐华东电力试验研究院

汤文明(1969-)，博士，教授，主要从事材料失效与可靠性评估工作，电话:0551-62901362，E-mail: wmtang69＠126.com

收稿日期: 2024-07-05

修回日期: 2023-09-12

录用日期: 2023-09-15

网络出版日期: 2024-11-14

收起

Mechanical Properties and Notch Sensitivities of the Hydrogenated X70 Pipeline Steel Welded Joints

Expand

(1.School of Materials Science and Engineering， Hefei University of Technology， Hefei 230009， China；2.Datang Boiler and Pressure Vessel Testing Center Co.， Ltd.， Hefei 230088， China；3.Datang East China Electric Power Test and Research Institute， Hefei 230088， China)

TANG Wenming(1969-)，Ph.D.，Professor，Research Focus:Material Failure and Reliability Assessment，Tel.:0551-62901362， E-mail: wmtang69＠126.com

Received date: 2024-07-05

Revised date: 2023-09-12

Accepted date: 2023-09-15

Online published: 2024-11-14

Fold

摘要

为探究管道内壁表面缺陷对长期输送掺氢天然气(HCNG)管线钢焊接接头的可靠性的影响，在X70 管线钢焊接接头的母材、焊缝及热影响区处开缺口，并对缺口部位进行电解渗氢，开展有、无渗氢X70 管线钢焊接接头缺口试样拉伸力学性能、显微组织及其缺口敏感性的测试分析。结果表明:渗氢导致X70 管线钢焊接接头试样的拉伸力学性能，尤其是塑性(断后延伸率A)的降低。由于缺口与氢损伤的叠加效应，缺口处组织未发生明显变形，拉伸断口呈准解理断裂特征。有、无渗氢X70 管线钢焊接接头均具有一定的缺口敏感性，渗氢致使焊接接头的缺口敏感性增大，渗氢焊缝的缺口敏感性较大，在管道检修时应予以关注。

关键词： X70 管线钢; 焊接接头; 电解渗氢; 缺口敏感性; 氢脆敏感性

本文引用格式

陈烨, 王万里, 占先强, 刘俊建, 汤文明 . 渗氢X70管线钢焊接接头的力学性能及缺口敏感性[J]. 材料保护, 2024 , 57(9) : 20 -27 . DOI: 10.16577/j.issn.1001-1560.2024.0197

Abstract

In order to explore the effects of pipeline inner-wall surface defects on reliability of the hydrogen enriched compressed natural gas(HCNG) pipeline steel welded joints in long-term service， the notches in the base metal， weld seam and heat affected zone of X70 pipeline steel welded joints were made，and the electrolytic hydrogen permeation on the notches was performed.Tests and analysis of the tensile mechanical properties， microstructures and notch sensitivities of the X70 pipeline steel welded joint notch samples with/without hydrogen permeation were carried out.Results showed that hydrogen permeation led to a decrease in the tensile mechanical properties of X70 pipeline steel welded joint samples， especially plasticity (elongation at break A).Due to the combined effect of notch and hydrogen damage， the tissue at the notch did not undergo significant deformation，and the tensile fracture exhibited quasi cleavage fracture characteristics.Furthermore，the welded joints of X70 pipeline steel with and without hydrogen permeation had certain notch sensitivity， and hydrogen permeation could increase the notch sensitivity of the welded joint.Therefore， the hydrogenated welding seams should be paid more attention during the pipeline maintenance， because of their higher notch sensitivity.

Key words： X70 pipeline steel; welded joint; electrolytic hydrogen permeation; notch sensitivity; hydrogen embrittlement sensitivity

Options

文章导航

模态框（Modal）标题

摘要

本文引用格式

Abstract