Study on the Corrosion Behavior of New Type of Acid Resistant Steel in Sulfuric Acid Containing Environment

  • HU Ling-ling ,
  • LI Min
Expand
  • 1. Department of Mechanical and Electrical Engineering, Hunan College of Information, Changsha 410200, China;
    2. China Railway Environment and Technology Engineering Co., Ltd., Changsha 410200, China

Received date: 2022-11-28

  Revised date: 2022-12-25

  Accepted date: 2023-01-26

  Online published: 2023-07-14

Abstract

In order to study the corrosion resistance and mechanism of a new type of acid resistant steel (LGNS-P) in sulfuric acid containing environments, Q345B carbon steel was used as a comparative material, and the corrosion behavior of two types of steels before and after the full immersion test was observed and tested through sulfuric acid accelerated corrosion test, corrosion weight loss analysis, SEM observation of corrosion morphology, and electrochemical potentiodynamic polarization tests. Results showed that the corrosion degree of LGNS-P was obviously less than Q345B, and the corrosion rate was gradually decreased during the test cycles. By contrast, the corrosion rate of Q345B increased first and then decreased, reaching its maximum after 240 h of testing. Compared to Q345B, the corrosion product layer of LGNS-P was more uniform and denser, which blocked the direct contact between corrosive ions and the substrate to some extent. In addition, there were some Fe oxides on the surface of both steels, but Sb oxides were also found on the surface of LGNS-P, which had certain acid resistance and could enhance the bonding ability of the corrosion product layer and the substrate. Overall, the above differences caused the significant improvement of acid corrosion resistance of LGNS-P

Cite this article

HU Ling-ling , LI Min . Study on the Corrosion Behavior of New Type of Acid Resistant Steel in Sulfuric Acid Containing Environment[J]. Materials Protection, 2023 , 56(6) : 89 -96 . DOI: 10.16577/j.issn.1001-1560.2023.0139

References

[1] 佘 锋, 张迎恺. 省煤器硫酸露点腐蚀的选材[J]. 石油化工设备技术, 2018, 39(1): 59-62.
SHE F, ZHANG Y K. Material selection for sulfuric acid dew point corrosion of economizers[J]. Petrochemical Equipment Technology, 2018, 39(1): 59-62.
[2] 孙继友. 新一代钢铁材料在铁路货车车辆上的应用探讨[J]. 中国科技信息, 2007(1): 90-91.
SUN J Y. Research on Application of new Generation of Iron and Steel Materials in Railway Rolling Stocks[J]. China Science and Technology Information, 2007(1): 90-91.
[3] WU B Y, LIANG W, WANG A H. Compositional design of low carbon sulphuric acid dewpoint corrosion resistant steel and corresponding anticorrosive mechanism[J]. British Corrosion Journal, 2013, 48(4): 313-320.
[4] 何春雨, 余 伟, 唐 荻. 铁路货车车体用钢的现状及研究发展趋势[J].热加工工艺, 2020, 49(16): 15-20.
HE C Y, YU W, TANG D. Current Situation and Research Development Trend of Railway Wagon Body Steel[J]. Hot Working Technology, 2020, 49(16): 15-20.
[5] XUE W, LI Z L, XIAO K, et al.Initial microzonal corrosion mechanism of inclusions associated with the precipitated (Ti, Nb) N phase of Sb-containing weathering steel[J].Corrosion Science, 2020, 163:108232.
[6] 柯 伟, 董俊华. Mn-Cu钢大气腐蚀锈层演化规律及其耐候性研究[J]. 金属学报, 2011, 46: 1 365-1 378.
KE W, DONG J H. Study on the rusting evolution and the performance of resisting to atmospheric corrosion for Mn-Cu steel[J]. Acta Metallurgica Sinica, 2011, 46: 1 365-1 378.
[7] SONG J L, CHEN J H, YI P, et al.Correlation between indoor and outdoor corrosion tests for coal train body steel in a coal medium environment[J].Journal of Iron and Steel Research International, 2022, 29(9):1 495-1 504.
[8] HONG J H, LEE S H, KIM J G, et al.Corrosion behavior of copper containing low alloy steels in sulfuric acid[J].Corrosion Science, 2012, 54(9):174-182.
[9] LE D P, JI W S, KIM J G, et al. Effect of antimony on the corrosion behavior of low-alloy steel for flue gas desulfurization system[J].Corrosion Science, 2008, 50(4):1 195-1 204.
[10] CHENG X Q , SUN F L, LV S J, et al. A new steel with good low temperature sulfuric acid dew point corrosion resistance[J].Materials and Corrosion, 2012, 63(7):598-606.
[11] PARDO A, MERINO M C, CARBONERAS M, et al. Influence of Cu and Sn content in the corrosion of AISI 304 and 316 stainless steels in H2SO4[J].Corrosion Science, 2006, 48(5):1 075-1 092.
[12] 郭明晓, 潘 晨, 王振尧, 等. 碳钢在模拟海洋工业大气环境中初期腐蚀行为研究[J]. 金属学报, 2018, 54(1): 65-75.
GUO M X, PAN C, WANG Z Y, et al. A Study on the Initial Corrosion Behavior of Carbon Steel Exposed to a Simulated Coastal-Industrial Atmosphere[J]. Acta Metallurgica Sinica, 2018, 54(1): 65-75.
[13] PARK S A, KIM S H,YOO Y H, et al. Effect of chloride ions on the corrosion behavior of low-alloy steel containing copper and antimony in sulfuric acid solution[J]. Metals and Materials International, 2015, 21(3): 470-478.
[14] 张 聪, 周 成, 叶先祥. 新型耐酸钢在硫酸盐酸混合溶液中的腐蚀行为[J]. 腐蚀与防护, 2015, 36(7): 599-602.
ZHANG C, ZHOU C, YE X X. The Corrosion Behavior of a New Acid Resistant Steel in a Concentrated Sulphuric Acid Solution Containing HCl[J]. Corrosion and Protection, 2015, 36(7): 599-602.
[15] JANG Y W, HONG J H, KIM J G . Effects of copper on the corrosion properties of low-alloy steel in an acid-chloride environment[J]. Metals and Materials International, 2009, 15(4):623-629.
[16] HE Y , YOO K B , PARK J C, et al. TEM study the corrosion behavior of the low alloy steels developed for flue gas desulfurization system[J]. Materials Characterization, 2018, 142:540-549.
[17] XIAO K, LI Z L, SONG J L, et al.Effect of Concentrations of Fe2+ and Fe3+ on the Corrosion Behavior of Carbon Steel in Cl- and SO42- Aqueous Environments[J].Metals and Materials International, 2021, 27:2 623-2 633.
[18] QIANG Y, DONG C F, FANG Y H, et al.Atmospheric Corrosion of Q235 Carbon Steel and Q450 Weathering Steel in Turpan,China[J].Journal of Iron and Steel Research, International, 2016, 23(10):1 061-1 070.
[19] ZHANG Q C, WU J S, WANG J J, et al.Corrosion behavior of weathering steel in marine atmosphere[J].Materials Chemistry and Physics, 2003, 77(2):603-608.
[20] LI Z L, XUE W, CHEN Y Q,et al.Microstructure and Grain Boundary Corrosion Mechanism of Pearlitic Material[J].Journal of Materials Engineering and Performance, 2022, 31:483-494.
[21] SUTER T, BOHNI H. Microelectrodes for corrosion studies in microsystems[J].Electrochimica Acta, 2001, 47: 191-199.
[22] 于海成, 何晓东, 刘咏咏,等. 浅析耐硫酸腐蚀用不锈钢的应用现状与发展[J]. 中国化工装备, 2017, 19(5): 35-40.
YU H C, HE X D, LIU Y Y, et al. Analysis for the Application Status and Development of Sulfuric Acid Corrosion Resistant Stainless Steel[J]. China Chemical Industry Equipment, 2017, 19(5): 35-40.
[23] LI Z L, XIAO K, DONG C F, et al.Atmospheric corrosion behavior of low-alloy steels in a tropical marine environment[J].Journal of Iron and Steel Research, International, 2019, 26:1 315-1 328.
[24] SONG J L, LI Z L, XIAO K, et al.Study on the local corrosion behaviour and mechanism of bogie steel welded joints[J]. Corrosion Science, 2022, 208:110 709.
[25] 叶先祥, 周 成, 张 聪. 新型耐硫酸盐酸露点腐蚀钢的性能研究[J]. 腐蚀科学与防护技术, 2015, 27(2): 135-140.
YE X X, ZHOU C, ZHANG C. Corrosion Performance of a New Low Alloy Steel Cu-Sb-Mo for Resisting Dew-point Corrosion Induced by Sulfuric Acid and Hydrochloric Acid[J]. Corrosion Science and Protection Technology, 2015, 27(2): 135-140.
[26] WU W, DAI Z, LIU Z, et al.Synergy of Cu and Sb to enhance the resistance of 3%Ni weathering steel to marine atmospheric corrosion[J].Corrosion Science, 2021, 183(9):109353.
[27] HERMAS A E A, ELNADY A M, ALI R M.Corrosion inhibition of stainless steel in sulfuric acid solution containing sulfide ions[J].Anti-Corrosion Methods and Materials, 2019, 66(3):360-368.
[28] LI J S, CHEN J H, SONG J L, et al. Research on Corrosion Behavior of Truck Body Steel in chlorine-containing sulfuric acid environment[J].Journal of Materials Research and Technology, 2022, 21:1 878-1 889.
[29] 王月香, 魏承志, 冯文义, 等. 低成本耐硫酸露点腐蚀高强钢板的试制开发[J]. 山东冶金, 2018, 40(1): 1-3.
WANG Y X, WEI C Z, FENG W Y, et al. Study and Trial Production of One Kind of Sulfuric Acid Dew-point Corrosion Resistance High-strength Steel Plates with Low-cost[J]. Shandong Metallurgy, 2018, 40(1): 1-3.
[30] YANG Y, JIANG C, CHENG X, et al.Effect of Sb on the Corrosion Behavior of Low-Alloy Steels in a Simulated Polluted Marine Atmosphere[J].Journal of Materials Engineering and Performance, 2020, 29(24):1-10.
Outlines

/