Effects of Magnetic Mark Display on Mechanical Properties of Laser-Enhanced 17-4PH Blades

Expand
  • Harbin Steam Turbine Factory Co.,Ltd.,Harbin 150000,China

Received date: 2022-08-27

  Revised date: 2022-09-15

  Accepted date: 2022-10-26

  Online published: 2023-02-15

Abstract

In order to enhance the corrosion resistance of the 17-4PH low-pressure last stage blades,the steam inlet side of the 17-4PH blades needs to be treated with laser-enhanced solid solution.The last stage blades treated with laser solution often show obvious magnetic marks in the subsequent magnetic particle inspection.Optical microscope,scanning electron microscope,X-ray diffractometer,electron probe and other analytical means were used to prove that the reason for the appearance of magnetic marks at the boundary of the laser solid solution region was a large number of austenite structures that appeared at the boundary,which reduced the permeability at the boundary of the laser solid solution region.Besides,the residual stress of laser solid solution blade was determined as compressive stress by XRD,and the three-point bending fatigue test showed that the R=0.1 fatigue limit of 17-4PH blade could be increased from 750 MPa to 860 MPa by laser-enhanced solid solution.

Cite this article

HAN Liang, GONG Wei-xing, FENG Tian-shu, WANG Jian-ze . Effects of Magnetic Mark Display on Mechanical Properties of Laser-Enhanced 17-4PH Blades[J]. Materials Protection, 2023 , 56(2) : 170 -174 . DOI: 10.16577/j.issn.1001-1560.2023.0048

References

[1] 路媛媛,肖 鱼,赖 境,等.激光固溶对17-4PH 不锈钢力学性能的影响[J].金属热处理,2019,44(2):156-162.LU Y Y,XIAO Y,LAI J,et al.Effect of laser solid solution treatment on mechanical properties of 17-4PH stainless steel[J].Heat Treatment of Metals,2019,44(2):156-162.

[2] 薛承感,潘慧斌,丁银萍,等.17-4PH 汽轮机叶片激光固溶强化抗汽蚀性能研究[J].动力工程学报,2020,40(1):82-88.XUE C G,PAN H B,DING Y P,et al.Cavitation Erosion Behavior of 17-4PH Steam Turbine Blades Treated by Laser Solid Solution[J].Journal of Chinese Society of Power Engineering,2020,40(1):82-88.

[3] 叶诗豪,姚建华,楼程华,等.17-4PH 不锈钢的激光表面固溶工艺研究[J].应用激光,2010,30(6):465-469.YE S H,YAO J H,LOU C H,et al.Study of Laser Surface Solid Solution Experiment on 17-4PH Stainless Steel[J].Applied Laser,2010,30(6):465-469.

[4] 曹 强,黄晓望,汪 盛.1Cr15Ni4Mo3N 沉淀硬化不锈钢磁粉检测疑似裂纹原因分析[J].失效分析与预防,2014,9(2):121-125.CAO Q,HUANG X W,WANG S.Analysis of Suspected Crack of 1Cr15Ni4Mo3N Precipitation-hardening Stainless Steel by Magnetic Part[J].Failure Analysis and Prevention,2014,9(2):121-125.

[5] 王树志,乔海燕,葛子亮,等.17-4PH 马氏体沉淀硬化不锈钢磁粉检测磁痕分析[J].无损检测,2014,36(1):64-70.WANG S Z,QIAO H Y,GE Z L,et al.The Indication Analysis of Magnetic Particle Testing on 17 -4PH Martensitic Precipitation-hardening Stainless Steel[J].Nondestructive Testing,2014,36(1):64-70.

[6] 陈 波.17-4PH 钢热变形特性与高温铁素体析出条件研究[D].上海:上海交通大学,2018.CHEN B.Study on the Thermal Defformation Characteristics of 17-4PH Steel and the Precipitation Conditions of δ-Ferrite[D].Shanghai:Shanghai Jiao Tong University,2018.

[7] 杜锦铮,路媛媛,陈 浩,等.17-4PH 不锈钢透平叶片激光固溶时效强化的力学性能[J].中国表面工程,2018,31(3):9-16.DU J Z,LU Y Y,CHEN H,et al.Mechanical Properties of 17-4PH Stainless Turbin Blades by Laser Solution and Aging[J].China Surface Engineering,2018,31(3):9-16.

Outlines

/