Effect of pH value on the Corrosion Behavior of 904L Stainless Steel Under High Cl- Concentration Environment

Expand
  • 1.China Petroleum Engineering & Construction Corp.,Beijing Company,Beijing 100085,China;2.PetroChina International Co.,Ltd.,Canada Branch,Beijing 100032,China;3.Institute for Advanced Materials and Technology,University of Science and Technology Beijing,Beijing 100083,China

Received date: 2023-02-22

  Revised date: 2023-03-12

  Accepted date: 2023-04-15

  Online published: 2023-08-23

Abstract

 For improving the corrosion resistance of 904L stainless steel under high Cl- concentration environment with different pH values condition,the corrosion behavior of 904L austenitic stainless steel in 100 g/L NaCl solution at different pH values was studied by cyclic polarization curves,electrochemical impedance spectroscopy,Olympus confocal microscopy,scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS).Results showed that the corrosion resistance of 904L stainless steel increased with the increase of pH value,EIS consisted of two capacitive reactance arcs,and the radius of capacitive reactance arc increased with the increase of pH value,and the capacitive reactances were all in the same order of magnitude.Meanwhile,lower pH value conditions could enhance the destructive effect of Cl- on the passive film.With the decrease of pH value,the range of passive region of the material decreased.When the pH=2,slight pitting occurred on the surface of the material.

Cite this article

ZHANG Hong, LI Yuanlong, WANG Jie, JIN Jie, FAN Xuehua, YANG Meng . Effect of pH value on the Corrosion Behavior of 904L Stainless Steel Under High Cl- Concentration Environment[J]. Materials Protection, 2023 , 56(7) : 77 -82 . DOI: 10.16577/j.issn.1001-1560.2023.0164

References

[1] 刘欣芳.904L 和254SMO 超级奥氏体不锈钢在高氯酸性环境中的点蚀行为研究[D].北京:北京化工大学,2017.LIU X F.Research on Pitting Behavior of 904L and 254SMO in High Cloride-Containing Acid Enviorment[D].Beijing:Beijing University of Chemical Technology,2017.

[2] LUO H,SU H,DONG C,et al.Influence of pH on the passivation behaviour of 904L stainless steel bipolar plates for proton exchange membrane fuel cells[J].Journal of Alloys and Compounds,2016,686: 216-226.

[3] WANG J,SHI W,XIANG S,et al.Study of the corrosion behaviour of sensitized 904L austenitic stainless steel in Clsolution[J].Corrosion Science,2021,181(68): 109234.

[4] MOAYED M H,NEWMAN R C.Aggressive effects of pitting “inhibitors”on highly alloyed stainless steels[J].Corrosion Science,1998,40(2): 519-522.

[5] AMAND S,MUSIANI M,ORAZEM M E,et al.Constant-Phase-Element Behavior Caused by Coupled Resistivity and Permittivity Distributions in Films[J].Electrochimica Acta,2013,87(1): 693-700.

[6] ORAZEM M E,FRATEUR I,TRIBOLLET B,et al.Dielectric Properties of Materials Showing Constant-Phase-Element (CPE) Impedance Response[J].Journal of The Electrochemical Society,2013,160(6): 215-225.

[7] WANG Z,FENG Z,ZHANG L.Effect of high temperature on the corrosion behavior and passive film composition of 316 L stainless steel in high H2S-containing environments[J].Corrosion Science,2020,174: 108844.

[8] WANG Z,ZHANG G H,FAN X H,et al.Corrosion behavior and surface characterization of an equiatomic CoCrFeMoNi high-entropy alloy under various pH conditions[J].Journal of Alloys and Compounds,2022,900: 163423.

[9] 安立聪,曹 静,李笑玲,等.合金元素Mo 和Mn 对铸态双相不锈钢在Cl-中点蚀行为的影响:2015 中国铸造活动周论文集[C].长沙:中国机械工程学会,2015:1-7.AN L C,CAO J,LI X L,et al.Effect of Mo and Mn Additions on the Pitting Corrosion Behavior of Duplex Stainless Cast-steels:Proceedings of 2015 China Casting Week[C].Changsha: Chinese Society of Mechanical Engineering,2015:1-7.
Outlines

/