Influence of CO2/O2 on the Corrosion Behavior of J55 Tubing Steel in the Water Injection Area of Dingbian Oilfield

LI Nan, YUAN Qing, BAI Yaowen, YIN Zhifu, LUO Ying, GAO Xiaoyan, ZHANG Yanting

doi:10.16577/j.issn.1001-1560.2023.0165

Materials Protection >

2023 , Vol. 56 >Issue 7: 83 - 89

DOI: https://doi.org/10.16577/j.issn.1001-1560.2023.0165

Influence of CO₂/O₂ on the Corrosion Behavior of J55 Tubing Steel in the Water Injection Area of Dingbian Oilfield

Expand

1.Dingbian Oil Plant，Yanchang Oil Field Co.，Ltd.，Yulin 719000，China；2.Shaanxi Key Laboratory of Surface Engineering and Remanufacturing，Xi’an University，Xi’an 710065，China

Received date: 2023-01-25

Revised date: 2023-02-15

Accepted date: 2023-03-12

Online published: 2023-08-23

Fold

Abstract

In order to clarify the influence of a large amount of aggressive CO2 and O2 contained in the oil well produced fluid in the water injection area of Dingbian oilfield on the corrosion behavior of tubing steel and reveal the corrosion characteristics，the electrochemical corrosion behaviors of J55 tubing steel in the oilfield water injection area in the simulated produced water of oil wells and saturated CO2/O2 simulated produced water of oil wells were studied by potentiodynamic polarization curve and electrochemical AC impedance test method，combined with the on-site corrosion hanging ring monitoring method.In addition，the corrosion rate of the sample was calculated by weight loss method，and the corrosion morphology characteristics and product composition of the sample were analyzed.Results showed that CO2 and O2 promoted the cathodic depolarization，and saturated CO2/O2 significantly increased the corrosion current density of J55 tubing steel.The increase of environment temperature accelerated the reaction kinetics，which significantly increased the corrosion current density，but weakened the erosion of CO2 and O2.At 25 °C，the samples exhibited inductive reactance characteristics in the low-frequency region in the simulated produced water of oil wells environment containing saturated CO2/O2，while the Warburg diffusion impedance characteristics occurred in the low-frequency region of the samples in the two media environments at 60 °C.Moreover，the upper tubing of on-site oil well was less corroded than the lower tubing，and the corrosion products were mainly iron oxides and hydroxides.

Key words： J55 tubing steel; CO₂/O₂corrosion; polarization curve; AC impedance; corrosion hanging ring

Cite this article

LI Nan, YUAN Qing, BAI Yaowen, YIN Zhifu, LUO Ying, GAO Xiaoyan, ZHANG Yanting . Influence of CO₂/O₂ on the Corrosion Behavior of J55 Tubing Steel in the Water Injection Area of Dingbian Oilfield[J]. Materials Protection, 2023 , 56(7) : 83 -89 . DOI: 10.16577/j.issn.1001-1560.2023.0165

References

[1] 戚建晶，何淼，尹志福，等.含H₂S/CO₂腐蚀环境下80S和80S-3Cr 抗硫油管材料的性能研究[J].材料保护，2021，54(7):63-68.QI J J，HE M，YIN Z F，et al.Study on the performance of anti-sulfur tubing materials 80S and 80S-3Cr in H2 S/CO2 corrosion environment[J].Materials Protection，2021，54(7): 63-68.

[2] 李彦鹏，朱世东，李金灵，等.油气管道H2S/CO2腐蚀与防护技术研究进展[J].腐蚀与防护，2022，43(6):1-6.LI Y P，ZHU S D，LI J L，et al.Research progress of H2S/CO2 corrosion and protection technology for oil and gas tubing[J].Corrosion ＆ Protection，2022，43(6): 1-6.

[3] 鲁群岷，岳波，龚智力.含CO₂ 油田介质环境中O2 对X80 钢腐蚀行为的影响[J].腐蚀与防护，2019，40(6):408-413.LU Q M，YUE B，GONG Z L.Effect of O2 on corrosion behavior of X80 steel in environment of oil field medium containing CO2[J].Corrosion ＆ Protection，2019，40(6):408-413.

[4] 姚彬，郭玉洁，曾文广，等.塔河油田某注采井生产油管腐蚀失效分析[J].石油与天然气化工，2014，48(4):69-73.YAO B，GUO Y J，ZENG W G，et al.Corrosion failure analysis of protection tubing of an injection well in Tahe oilfield [J].Chemical Engineering of Oil ＆ Gas，2014，48(4): 69-73.

[5] 刘婉颖，李金宇，高科超，等.温度对N80 钢在饱和CO2模拟地层水下腐蚀行为的影响及机理[J].表面技术，2022，51(8):353-362.LIU W Y，LI J Y，GAO K C，et al.Effect and mechanism of temperature on the corrosion behavior of N80 steel in simulated formation with saturated CO2[J].Surface Technology，2022，51(8): 353-362.

[6] 王月，王丹，谢飞，等.CO2 对油田地下水环境中Q235 钢和X70 钢腐蚀行为的影响[J].金属热处理，2020，45(6):226-231.WANG Y，WANG D，XIE F，et al.Effect of CO2 corrosion behavior of Q235 steel and X70 steel in oilfield groundwater environment[J].Heat Treatment of Metals，2020，45(6):226-231.

[7] 葛睿，张钧.N80 油管钢在模拟油田CO2环境中的腐蚀行为[J].焊管，2019，42(8):1-6.GE R，ZHANG J.Corrosion behavior of N80 tubing steel in simulated oilfield CO2 environment[J].Welded Pipe and Tube，2019，42(8):1-6.

[8] 王虎，任燮东，王平.高温高压CO2腐蚀产物膜生长的原位电化学研究:第十一届全国腐蚀与防护大会论文摘要集[C].沈阳:中国腐蚀与防护学会，2021:51-52.WANG H，REN X D，WANG P.In-situ electrochemical study on the growth of CO2 corrosion product film at high temperature and high pressure:Abstracts of the 11th National Conference on Corrosion and Protection[C].Shengyang:China Society for Corrosion and Protection，2021:51-52.

[9] 代龙威.川气东送天然气管道材料CO2 腐蚀机理研究[J].材料保护，2021，54(5):57-62.DAI L W.Research of CO2 corrosion mechanism of natural gas pipeline materials from Sichuan to East[J].Materials Protection，2021，54(5):57-62.

[10] 李臻，邱婕，周晓义，等.高温高压CO₂/O₂ 共存流体中N80 钢腐蚀特性分析[J].西安石油大学学报(自然科学版)，2022，37(2):118-124.LI Z，QIU J，ZHOU X Y，et al.Corrosion characteristics of N80 steel in high-temperature high-pressure CO2/O2 coexisting fluid[J].Journal of Xi’an Shiyou University (Natural Science Edition)，2022，37(2): 118-124.

[11] 孙永涛，付朝阳，杨秀兰.高温多元热流体注采中管材腐蚀分析[J].石油与天然气化工，2012，41(4):408-410.SUN Y T，FU C Y，YANG X L，et al.Corrosion analysis，oil pipe in injection exploitation of high temperature multicomponent thermal fluid[J].Chemical Engineering of Oil ＆Gas，2012，41(4): 408-410.

[12] 赵国仙，王映超，张思琦，等.H2S/CO2对J55 钢腐蚀的影响机制[J].中国腐蚀与防护学报，2022，42(5):785-790.ZHAO G X，WANG Y C，ZHANG S Q，et al.Influence mechanism of H2S/CO2-charging on corrosion of J55 steel in an artificial solution[J].Journal of Chinese Society of Corrosion and Protection，2022，42(5):785-790.

[13] HSU C H，MANSFELD F.Technical note: concerning the conversion of the constant phase element parameter Y0 into a capacitance[J].Corrosion，2001，57(9): 747-748.

Options

Outlines

模态框（Modal）标题

Abstract

Cite this article

References