Study of Initial Corrosion Behavior of Typical Wheel Steel in Neutral Salt Spray Environment

Expand
  • (1.Research Institute of Technology of Shougang Group Co., Ltd., Beijing 100043, China;2.Beijing Key Laboratory of Green Recyclable Process for Iron & Steel Production Technology, Beijing 100043, China;3.Shougang Jingtang United Iron and Steel Co., Ltd., Tangshan 063200, China)

Received date: 2023-03-21

  Revised date: 2023-04-12

  Accepted date: 2023-05-16

  Online published: 2023-09-15

Abstract

In order to solve the problem of atmospheric corrosion of wheel steels during their service,the initial corrosion behaviors of two kinds of automotive wheel steels 590CL and 780CL at 590 MPa and 780 MPa levels in neutral salt spray environment of 5% NaCl solution were studied by neutral salt spray test.The morphology, structure, corrosion rate and electrochemical behavior of corrosion products after salt spray test were characterized by glow spectrometer, metallographic microscope, scanning electron microscope (SEM), X-ray diffractometer (XRD)and electrochemical measurement.Results showed that after 48 h in the neutral salt spray test, red rust appeared on the surface of the two wheel steels, and the corrosion rates of the two were 590CL>780CL.The polarization curves and electrochemical impedance spectroscopy results measured in 3.5%NaCl solution were in good agreement with the above results.Besides, the corrosion products of 590CL and 780CL steels were mainly γ-FeO(OH), and also contained some α-FeO(OH) and Fe3O4.However, the corrosion products basically had no protective effect on the substrate.

Cite this article

LI Haoyuan, WANG Shanshan, ZHANG Dawei, XIAO Baoliang, WEI Yangen . Study of Initial Corrosion Behavior of Typical Wheel Steel in Neutral Salt Spray Environment[J]. Materials Protection, 2023 , 56(9) : 90 -97 . DOI: 10.16577/j.issn.1001-1560.2023.0217

References

[1] Hernández F C R, DEMAS N G, DAVIS D D, et al.Mechanical properties and wear performance of premium rail steels[J].Wear, 2007, 263(1-6): 766-772.

[2] 郑文龙.钢的腐蚀磨损失效及其分析方法[C]/ /石油和化工设备管道防腐技术与对策专题研讨会文集.厦门:中国石油石化工程研究会,2010:21-43.ZHENG W L.Corrosion and wear failure of steel and its analysis method[C]/ /Proceedings of the National Petroleum and Chemical Industry Corrosion and Protection Technology Exchange Conference.Xiamen: China Petroleum and Petrochemical Engineering Research Association,2010:21-43.

[3] EKBERG A, Åkesson B, KABO E.Wheel/rail rolling contact fatigue-Probe, predict, prevent[J].Wear,2014,314:2-12.

[4] ZENG D, LU L, ZHANG J, et al.Effect of micro-inclussions on subsurface-initiated rolling contactfatigue of a railway wheel[J].Journal of Rail and Rapid Transit, 2016,230(2): 544-553.

[5] 郭明晓, 潘 晨, 王振尧,等.碳钢在模拟海洋工业大气环境中初期腐蚀行为研究[J].金属学报, 2018, 54(1):65-75.GUO M X, PAN C, WANG Z Y, et al.A study on the initial corrosion behavior of carbon steel exposed to a simulated coastal-industrial atmosphere[J].Acta Metallurgica Sinica,2018, 54(1): 65-75.

[6] 张 琳, 王振尧, 赵春英,等.碳钢和耐候钢在盐雾环境下的腐蚀行为研究[J].装备环境工程, 2014, 11(1):1-6.ZHANG L, WANG Z Y, ZHAO C Y, et al.Study on corrosion behavior of carbon steel and weathering steel in salt spray test [J].Equipment Environmental Engineering,2014, 11(1): 1-6.

[7] 金泉军,梁 韬,吕玲芳,等.不同腐蚀试验方法对镀锌材料的防腐性能评价研究[J].材料保护,2023,56(2):51-56.JIN Q J, LIANG T, LV L F, et al.Evaluation of the anticorrosion performance of galvanized materials using different corrosion test methods [J].Materials Protection, 2023,56(2): 51-56.

[8] 吴 菲,肖 峰,江 波,等.C 和Si 含量对车轮钢腐蚀行为的影响[J].腐蚀与防护,2017,38(2):124.WU F, XIAO F, JIANG B, et al.Effects of C and Si content on corrosion behavior of wheel steel[J].Corrosion &Protection, 2017,38(2):124.

[9] 曾 伟,王少杰,韩 靖,等.预腐蚀对ER8 车轮钢磨损行为的影响[J].材料导报, 2019, 33(24): 4 152-4 156.ZENG W, WANG S J, HAN J, et al.Effect of pre-corrosion on wear behavior of ER8 wheel steel[J].Materials Reports, 2019, 33(24): 4 152-4 156.

[10] 杨文斌,夏金龙,肖 乾,等.ER8 车轮钢激光熔覆涂层在酸雨环境下的磨损与腐蚀性能分析研究[J].表面技术,2023, 52(1): 314-324.YANG W B,XIA J L,XIAO Q,et al.Performance analysis of laser cladding coating on ER8 wheel steel in acid rain environment [J].Surface Technology, 2023, 52 ( 1):314-324.

[11] 黎 敏,郝玉林,姚士聪,等.中性盐雾环境中典型汽车用钢的初期腐蚀行为[J].电镀与涂饰, 2019, 38(18):1 015-1 021.LI M, HAO Y L, YAO S C, et al.Early corrosion behavior of typical automotive steel sheets in neutral salt spray test[J].Electropating & Finishing, 2019, 38 ( 18):1 015-1 021.

[12] 黄 雄,朱春东,于凤群.DP590 双相高强钢焊缝在模拟酸雨溶液中的腐蚀行为[J].热加工工艺,2017,46(17):187-190.HUANG X, ZHU C D, YU F Q.Corrosion behavior of DP590 dual-phase high-strength steel welding seam in simulated acid rain solution[J].Hot Working Technology,2017,46(17):187-190.

[13] 韩军科,严 红,黄 耀,等.耐候钢表面氧化皮的结构特征及其对大气腐蚀行为的影响[J].金属学报,2017,53(2):163-174.HAN J K, YAN H, HUANG Y, et al.Structural features of oxide scales on weathering steel and their influence on atmospheric corrosion[J].Acta Metallurgica Sinica, 2017,53(2):163-174.

Outlines

/