The corrosion problems of essential service water system in nuclear power plant directly affect the system integrity and availability, thus threatening the safety operation power of plant. In order to control and avoid corrosion problems, in this paper, two aspects of the failure cases about internal anti-corrosive layer and the stainless steel material were summarized and analyzed. Results showed that the main reasons for the failure of the anti-corrosive layer were unreasonable construction and installation, natural aging. The main reasons for the failure of stainless steel structural components were improper material selection, structural design, and material processing technology. In response to the above failure issues, it was proposed to carry out work from two aspects: on-site construction quality control and post maintenance management to control the failure of anti-corrosive layer. Through material selection and replacement, structural improvement, and material inspection, corrosion defects of stainless steel components could be treated and prevented, which could provide reference for the corrosion management of essential service water systems in domestic nuclear power plants.
YANG Hong-huan
,
GAO Chao
,
PU Jing-jing
,
LIAO Xue-bo
,
PAN Yao-fan
. Analysis and Management Advice of Common Corrosion Behavior for Essential Service Water System in Nuclear Power Plant[J]. Materials Protection, 2023
, 56(6)
: 182
-185
.
DOI: 10.16577/j.issn.1001-1560.2023.0150
[1] 彭 超. 压水堆机组和示范快堆机组重要厂用水系统设计方案对比分析[J]. 给水排水,2018,54(增刊1):106-110.
PENG C. Comparison and analysis of important auxiliary water system design schemes for PWR and Demonstration Fast Reactor units[J]. Water & Wastewater Engineering, 2018,54(S1):106-110.
[2] 赵万祥,孔全兴,李伟光,等.核电站重要厂用水系统的腐蚀分析[J]. 全面腐蚀控制,2017,31(4):11-14.
ZHAO W X, KONG Q X, LI W G, et al. Corrosion Analysis of Essentail Service Water System for The Nuclear Plant[J]. Total Corrosion Control,2017,31(4):11-14.
[3] 彭文山, 侯 健, 刘少通,等.含砂海水中环氧树脂/Q235钢体系的冲刷腐蚀行为研究[J]. 表面技术,2021,50(4):335-343.
PENG W S, HOU J, LIU S T, et al. Erosion-corrosion Behavior of Epoxy Resin/Q235 Steel System in Flowing Seawater Containing Sand Particles[J]. Surface Technology,2021,50(4):335-343.
[4] 刘飞华, 任 爱, 杨 帆,等. 核电站海水冷却系统的腐蚀与防腐蚀设计[J]. 腐蚀与防护, 2007,28(6):313-316.
LIU F H, REN A, YANG F, et al. Corrosion and protection design of sea water cooling system in npp[J] .Corrosion & Protection, 2007,28(6):313-316.
[5] 刘飞华,晏卫国.大亚湾核电站核岛重要厂用水系统(SEC)典型的腐蚀事件及评价[J].腐蚀与防护,2007,28(12):633-636.
LIU F H, YAN W G. Typical corrosion faliure and its assessment of essent ail service water system for nuclear island in Daya Bay npp[J].Corrosion & Protection, 2007,28(12):633-636.
[6] 蒋林中.重要厂用水系统阀门腐蚀原因分析及处理[J].全面腐蚀控制,2015,29(9):73-75.
JIANG L Z. Cause Analysis and Treatment of Corrosion of Valves in Essential Service Water Systemina Power Plant[J]. Total Corrosion Control,2015,29(9):73-75.
[7] 杨树凯,尤 涛,林 斌,等.核电站大修期间阴极保护系统故障分析与维护策略[J].腐蚀与防护,2020,41(12):44-47.
YANG S K, YOU T, LIN B, et al. Failure Analysis and Maintenance Strategy for Cathodic Protection System during Overhaul of Nuclear Power Plant[J]. Corrosion & Protection, 2020,41(12):44-47.
[8] 赖春晓. 涂膜起泡和剥离的形成机理及防止方法[J].全面腐蚀控制, 2002,16(2):15-18.
LAI C X. Forming mechanism and preventing method of film blistering and peeling[J]. Total Corrosion, 2002,16(2): 15-18.
[9] 孔全兴,赵万祥,蒋林中,等. 重要厂用水系统管道橡胶衬里脱落原因分析[J]. 合成材料老化与应用,2014,43(4):44-48.
KONG Q X,ZHAO W X, JIANG L Z, et al. Essential Service Water Pipe Rubber Lining Drop Cause Analysis[J]. Synthetic Materials Aging and Application,2014,43(4):44-48.
[10] 庞启财. 防腐蚀涂料涂装和质量控制[M]. 北京:化学工业出版社,2003:37-41.
PANG Q C. Anti-corrosion coating and quality control[M]. Beijing: Chemical Industry Press, 2003: 37-41.
[11] 李 焱. 防腐蚀涂层的失效分析[J]. 上海涂料, 2008,46(9):36-39.
LI Y. Failure Analysis of Anti-corrosive Coats Shanghai Coatings[J]. Shanghai Coatings, 2008,46(9):36-39.
[12] 许少炳,梁耀升.循环水过滤系统反冲洗管衬胶管理[J].全面腐蚀控制,2014,28(10):47-49.
XU S B, LIANG Y S. Circulating Water Filtration System Backwash Pipe with Rubber Management Total[J]. Total Corrosion Control,2014,28(10):47-49.
[13] 胥 鑫. 国内某核电站生产准备阶段的设备腐蚀问题及对策研究[J].涂料技术与文摘,2012,33(11):17-24.
XU X. Equipment Corrosion Problem of Domestic Nuclear Power Station under Construction and Its Countermeasure[J]. Coatings Technology & Abstracts, 2012,33(11):17-24.
[14] 杨 晓. 17-4PH不锈钢性能和组织研究[D]. 哈尔滨:哈尔滨工程大学, 2007:24-31.
YANG X. The Properties and Macrostructures of 17-4 PH Stainless Steel[D]. Harbin: Harbin Engineering University, 2007:24-31.
[15] 肖纪美. 腐蚀电化学原理[M]. 北京:化学工业出版社,2002:44-47.
XIAO J M. Principle of corrosion electrochemistry[M]. Beijing: Chemical Industry Press, 2002:44-47.
[16] 魏宝明. 金属腐蚀理论及应用[M]. 北京:化学工业出版社,1984:153-154.
WEI B M. Theory and application of metal corrosion[M]. Beijing: Chemical Industry Press, 1984: 153-154.
[17] 李敏风. 钢结构表面处理标准和质量评定[J]. 电镀与涂饰,2016,30(1):49-52.
LI M F. Standard and quality assessment for the surface treatment of steel structure[J]. Electroplating & Finishing,2016,30(1):49-52.