Research on Prediction Method of Corrosion Rate of Gas Wells with Same Pressure of Tubing and Casing in Bohai Oilfield

Expand
  • (1.CNOOC (China) Co., Ltd., Beijing 100007, China;2.Engineering Technology Branch, CNOOC Energy Development Co., Ltd., Tianjin 300452, China;3.School of Earth Sciences, China Univerisity of Petroleum, Beijing 102249, China)

Received date: 2023-03-18

  Revised date: 2023-04-17

  Accepted date: 2023-05-18

  Online published: 2023-09-15

Abstract

At the beginning of the 21st century,a large number of oil and gas wells were put into operation in Bohai E oilfield.With the production of the oilfield entering the middle and late stage,the phenomenon of annulus pressure is common in gas wells,severe situations may develop into same pressure of tubing and casing, causing serious pipe corrosion hazards and serious safety issues such as oil and gas leakage and environmental pollution.In order to ensure the production safety of old wells and break through the technical limitations in stimulation operation,in this paper the influence of different factors on the corrosion rate of oil and gas well tubing was investigated, the statistics on the operation of five gas wells in Bohai E oilfield were conducted, the types of media that might cause corrosion were discussed.The integrity of the oil casing body was tested using different methods.Based on indoor experimental results and actual conditions, the corrosion rate of the oil casing in the above five gas wells was predicted, which would provide a basis for determining the degree of oil casing corrosion.

Cite this article

HE Pengfei, SONG Zhichao, WAN Xiang, XU Tong, CAO Yulin . Research on Prediction Method of Corrosion Rate of Gas Wells with Same Pressure of Tubing and Casing in Bohai Oilfield[J]. Materials Protection, 2023 , 56(9) : 177 -181 . DOI: 10.16577/j.issn.1001-1560.2023.0229

References

[1] NACE RP0204-2004,Stress Corrosion Cracking (SCC) Direct Assessment Methodology[S].

[2] 陈 尧,白真权.13Cr 和N80 钢高温高压抗腐蚀性能比较[J].石油与天然气化工,2007,36(3):239-246.CHEN Y, BAI Z Q.Comparison of High Temperature and High Pressure Corrosion Resistance between 13Cr and N80 Steels[J].Chemical Engineering of Oil & Gas,2007,36(3):239-246.

[3] 王志龙,艾俊哲,梅 平,等.二氧化碳对钢腐蚀的影响因素研究[J].油气田环境保护,2004,1(1):48-50.WANG Z L, AI J Z, MEI P, et al.Study on the influencing factors of carbon dioxide on steel corrosion[J].Environmental Protection of Oil & Gas Fields,2004,1(1):48-50.

[4] 李小龙,李学胜,刘志刚,等.不同CO2分压下油田产出液温度对N80 钢油管腐蚀的影响[J].材料保护,2013,46(10):60-61.LI X L, LI X S, LIU Z G, et al.The effect of oil field output fluid temperature on N80 steel tubing corrosion under different CO2 partial pressures[J].Materials Protection,2013,46(10):60-61.

[5] 朱世东,白真权,尹成先,等.P110 钢抗冲刷腐蚀行为研究[J].材料工程,2009(8):28-32.ZHU S D, BAI Z Q, YIN C X, et al.Research on Erosion and Corrosion Resistance of P110 Steel[J].Journal of Materials Engineering,2009(8):28-32.

[6] 朱世东,白真权,刘 会,等.Ca2+、Mg2+对N80 钢腐蚀速率的影响[J].腐蚀与防护,2008,29(12):724-726.ZHU S D, BAI Z Q, LIU H, et al.The Effect of Ca2+and Mg2+on the Corrosion Rate of N80 Steel[J].Corrosion &Protection,2008,29(12):724-726.

[7] 朱景龙,孙 成,王 佳,等.CO2 腐蚀及控制研究进展[J].腐蚀科学与防护技术,2007,19(5):350-353.ZHU J L, SUN C, WANG J, et al.Advances on research of CO2 induced corrosion and its protection[J].Corrosion Science and Protection Technology,2007,19(5):350-353.

[8] 赵国仙,吕祥鸿,韩 勇.流速对P110 钢腐蚀行为的影响[J].材料工程,2008(8):5-8.ZHAO G X, LV X H, HAN Y.Effect of Flow Rate on the Corrosion Behavior of P110 Steel[J].Journal of Materials Engineering,2008(8):5-8.

Outlines

/