Effect of MgO Nano - Particles on the Corrosion Resistance of Anodic Oxidation Film on Magnesium Alloy

Expand
  • (School of Mechanical and Power Engineering, Shenyang University of Chemical Technology, Shenyang 110142, China)

Received date: 2022-02-21

  Revised date: 2022-03-29

  Accepted date: 2022-04-21

  Online published: 2023-12-17

Fold

Abstract

In order to improve the corrosion resistance of the anodic oxidation film on magnesium alloy，an anodic oxidation film was fabricated on the surface of magnesium alloy by adding MgO nano - particles into the silicate alkaline electrolyte. The effects of MgO nano - particles on the surface morphology, phase composition and thickness of the anodic oxidation film were analyzed by optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), film thickness meter and X - ray diffraction (XRD). Besides, the effect of MgO nano - particles on the corrosion resistance of the anodic oxidation film was analyzed by dropping test and 3.5% NaCl immersion corrosion test. Results showed that adding MgO nano - particles into the electrolyte could reduce the number of micropores in the film and increase its density, thickness and MgO content, thus improving the corrosion resistance of the film.

Key words： magnesium alloy; anodic oxidation; MgO nano - particles; corrosion resistance

Cite this article

FU Guang - yan, CHEN Zhao - su, JIANG Tian - qi, LIU Hua - cheng, REN Lei . Effect of MgO Nano - Particles on the Corrosion Resistance of Anodic Oxidation Film on Magnesium Alloy[J]. Materials Protection, 2022 , 55(8) : 130 -133 . DOI: 10.16577/j.issn.1001-1560.2022.0226

Options
Outlines

/

〈 〉

Total visitors: 　Visitors of today: 　Now online:
Website Copyright © Editorial Department of Materials Protection
Powered by Beijing Magtech Co. Ltd,.