In order to investigate the friction and wear characteristics of nitride coatings on surface of WC cemented carbide and their effect on tool milling performance, TiN, CrN and TiAlN nitride coatings were deposited on surface of WC cemented carbide by physical vapor deposition (PVD). The microstructure and friction and wear properties of WC cemented carbide substrate and three nitride coatings were analyzed by means of scanning electron microscope (SEM), X-ray diffraction (XRD) and friction and wear tester. The milling performance of WC cemented carbide and three nitride coated cutting tools was studied by using 45 steel as the milling material. Results showed that the nitride coating could effectively improve the surface hardness and wear resistance of WC cemented carbide substrate. Among the three nitride coatings, TiAlN coating had the highest hardness, which was 26.5% higher than that of WC substrate, and significantly improved the wear resistance of WC cemented carbide. The wear characteristics of TiAlN coating were small abrasive wear and slight oxidation wear. The high hardness and high wear resistance of TiAlN coating were more conducive to milling 45 steel. The oxide film generated in the milling process was easy to cover the surface of the tool tip, playing a significant role in protecting the tool surface and further improving the milling performance of the tool. Compared with other coatings, TiAlN coated tools had less chip adhesion on the back face of the tool, and showed strong chip removal ability, which was of great significance to improve the milling performance of the tool.
SHAO Shu-feng
,
CHENG Xian-ming
,
SUN Shou-Yu
,
YANG Ke
,
FENG Yuan
. Study on Friction and Wear Characteristics of Coating on Surface of WC Cemented Carbide and Its Milling Performance[J]. Materials Protection, 2023
, 56(5)
: 97
-105
.
DOI: 10.16577/j.issn.1001-1560.2023.0112
[1] PASKVALE S,Remškar M, Čekada M. Tribological performance of TiN, TiAlN and CrN hard coatings lubricated by MoS2 nanotubes in Polyalphaolefin oil[J]. Wear, 2016, 352: 72-78.
[2] BIDESH B, SOURJYADEEP C, ANJANA J, et al. Secondary phase limited metal-insulator phase transition in chromium nitride thin films[J]. Acta Materialia, 2022, 227: 117 737.
[3] UDDIN G M, JOYIA F M, GHUFRAN M, et al. Comparative performance analysis of cemented carbide, TiN, TiAlN, and PCD coated inserts in dry machining of Al 2024 alloy[J]. The International Journal of Advanced Manufacturing Technology, 2021,112: 1 461-1 481.
[4] 王 欣,范其香,王铁钢,等. CrAlN 纳米复合涂层的组织结构及切削性能研究[J]. 材料保护,2021, 54(4): 63-68.
WANG X, FAN Q X, WANG T G,et al. The Microstructure and cutting property of CrAlN nanocomposite coating [J]. Materials Protection, 2021, 54(4): 63-68.
[5] 段佳妮,李文正,赵春蕾,等.多弧离子镀制备TiAlCN和TiAlN涂层的结构和摩擦磨损性能[J].表面技术, 2022, 51(4): 139-148.
DUAN J N, LI W Z, ZHAO C L, et al. Structure and tribological property ofTiAlCN and TiAlN coatings prepared by multi-arc ion plating[J]. Surface Technology, 2022, 51(4): 139-148.
[6] 李 祥,郑光明,盖少磊,等.PVD-AlTiN涂层刀具高速干铣削高温合金的磨损机理研究[J].工具技术, 2023, 57(1): 25-29.
LI X, ZHENG G M, GAI S L, et al. Wear mechanism of PVD-AlTiN cotated cutting tools in high-speed dry milling of superalloys[J]. Tool Engineering, 2023, 57(1): 25-29.
[7] XIAO Y, XIONG J, GUO Z X, et al. Microstructures and properties of PVDTiAlN coating deposited on cermets with different Ti(C, N) grain size[J]. Journal of Central South University: Science & Technology of Mining and Metallurgy, 2020, 27(2): 721-735.
[8] 梁 愉,李 钰,赵敏霞,等.TiAlN涂层对钛合金的热腐蚀防护作用研究[J].材料研究与应用, 2022, 16(6): 928-933.
LIANG Y,LI Y, ZHAO M X, et al. Study on hot corrosion protection effect of TiAlN coating on titanium alloy[J]. Materials Research and Application, 2022, 16(6): 928-933.
[9] 王建波,王润宇,张明恩,等.TiN和TiAlN涂层改善E690钢摩擦磨损性能的研究[J].热加工工艺, 2022, 51(14): 116-120.
WANG J B, WANG R Y, ZHANG M E, et al. Study on improvement of friction and wear properties of E690 steel by TiN and TiAlN coatings[J]. Hot Working Technology, 2022, 51(14): 116-120.
[10] 张 岚,张 博,廖 斌,等.固态NaCl诱导的TiAlN多层涂层热腐蚀行为研究[J].北京师范大学学报(自然科学版), 2022, 58(5): 720-726.
ZHANG L, ZHANG B, LIAO M, et al. High temperature corrosion of TiAlN multilayer coatings by solid NaCl[J]. Journal of Beijing Normal University(Natural Science), 2022, 58(5): 720-726.
[11] DAS S, GUHA S, GHADAI R, et al. A comparative analysis over different properties of TiN, TiAlN and TiAlSiN thin film coatings grown in nitrogen gas atmosphere[J]. Materials Chemistry and Physics, 2021, 258: 123 866-123 878.
[12] ADESINA A Y, GASEM Z M, MOHAMMED A S. Comparative investigation and characterization of the scratch and wear resistance behavior of TiN, CrN, AlTiN and AlCrN cathodic arc PVD coatings[J]. Arabian Journal for Science and Engineering, 2019, 44(12): 10 355-10 371.
[13] ZHENG G M, ZHAO G Y, CHENG X, et al. Frictional and wear performance of TiAlN/TiN coated tool against high-strength steel[J]. Ceramics International, 2018, 44(6): 6 878-6 885.
[14] KUMAR DD, KUMAR N, KALAISELVAM S, et al. Wear resistant super-hard multilayer transition metal-nitride coatings[J]. Surfaces and Interfaces, 2017(7): 74-82.
[15] CHAUS A S, SITKEVICH M V, Pokorny′ P, et al. Wear resistance and cutting performance of high-speed steel ball nose end mills related to the initial state of tool surface[J]. Wear, 2021, 472: 20 3711.
[16] CHANG K S, DONG Y J, ZHENG G M, et al. Friction and wear properties of TiAlN coated tools with different levels of surface integrity[J]. Ceramics International, 2022, 48(4): 4 433-4 443.
[18] WU J X, GANG Z, LIN H, et al. Tribological performance of micro-Groove tools of improving tool wear resistance in turning AISI 304 process[J]. Materials, 2020, 13(5): 1 236.