In order to obtain high-density 316L/IN718 mixed metal powder parts, the forming process of 316L/IN718 mixed metal powder was investigated by single fusion channel experiments, single layer experiments and block experiments, based on laser-selective melting (SLM) technology with different laser scanning speeds and scanning pitchs, respectively. Results showed that when 0.54 J/mm ≤ laser line energy density (L) ≤ 0.76 J/mm in a single melt experiment, the effect of melt forming is relatively good. When the laser power (P)=200 W, scanning speed (v) = 280 mm/s, and scanning pitch = 0.12 mm, the blocks with a density of 99.99% could be obtained. Besides, the laser energy density-relative density relationship was obtained by fitting. The process research presented application and promotion value, providing important experimental data and technical support for achieving forming gradient functional materials.
YANG Xuan
,
HAN Bao-hong
,
HE Wan-heng
,
ZHANG Dun-xu
. Study on Laser-Selective Melting Forming Process of 316L/IN718 Mixed Powder[J]. Materials Protection, 2023
, 56(5)
: 133
-138
.
DOI: 10.16577/j.issn.1001-1560.2023.2001
[1] 董定乾,向 新,顾金宝,等.梯度硬质合金制备技术及研究现状[J].硬质合金,2019,36(5):392-398.
DONG D Q, XIANG X, GU J B, et al.The Fabrication Technique and Research Status of Gradient Cemented Carbide[J]. Cemented Carbide,2019,36(5):392-398.
[2] 张争艳. 异质多材料零件快速成型关键技术研究[D].武汉:武汉理工大学,2014.
ZHANG Z Y. Research on the key technology of rapid prototyping of heterogeneous multi-material parts[D].Wuhan: Wuhan University of Technology,2014
[3] 赵 彻. 异质材料与微结构耦合仿生设计及其3D打印[D].长春:吉林大学,2017.
ZHAO C. Heterogeneous material and microstructure coupled bionic design and its 3D printing [D].Changchun: Jilin University,2017.
[4] BADER C,OXMAN N. Recursive symmetries for geometrically complex and materially heterogeneous additive manufacturing[J]. Computer-Aided Design,2016,81:39-47.
[5] 何季麟,张宗国.中国钽铌工业的现状与发展[J].中国金属通报,2006(48):2-8.
HE J L, ZHANG Z G. Status and development of tantalum-niobium industry in China[J]. China Metal Bulletin,2006(48):2-8.
[6] 席明哲,张永忠,涂 义,等.激光快速成形316L不锈钢/镍基合金/Ti6A14V梯度材料[J].金属学报,2008(7):826-830.
XI M Z, ZHANG Y Z, TU Y, et al. 316L STAINLESS STEEL/Ni-BASED ALLOY/Ti6Al4V GRADIENT MATERIALS PREPARED BY LASER RAPID FORMING PROCESS[J]. Acta Metallurgica Sinica,2008(7):826-830.
[7] GRIFFITH M L,SCHLIENGER M E,HARWELL L D,et al. Understanding thermal behavior in the LENS process[J]. Materials and Design,1999,20(2):107-113.
[8] ZHONG M L,LIU W J,YAO K F,et al. Microstructural evolution in high power laser cladding of Stellite 6+WC layers[J]. Surface and Coatings Technology,2002,157(2):128-137.
[9] LIN X, YUE T M,YANG H O,et al. Laser rapid forming of SS316L/Rene88DT graded material[J]. Materials Science & Engineering A,2004,391(1):325-336.
[10] LIN X, YUE T M,YANG H O,et al. Solidification Behavior and the Evolution of Phase in Laser Rapid Forming of Graded Ti6Al4V-Rene88DT Alloy[J]. Metallurgical and Materials Transactions A,2007,38(1):127-137.
[11] BI J,LEI Z L,CHEN Y B,et al . Effect of process parameters on formability and surface quality of selective laser melted Al-Zn-Sc-Zr alloy from single track to block specimen[J]. Optics and Laser Technology,2019,118:132-139.