Effect of Different Heat Treatment States on Chemical Milling Properties of 2195 Al-Li Alloy

Expand
  • Sichuan Aerospace Long March Equipment Manufacturing Co. Ltd., Chengdu 610100, China

Received date: 2022-07-30

  Revised date: 2022-08-13

  Accepted date: 2022-09-25

  Online published: 2023-07-25

Abstract

For studying the effect of different heat treatment states on the chemical milling properties of 2195 Al-Li alloy, orthogonal experiments were used to research the chemical milling properties of 2195 Al-Li alloys with different heat treatment states(T8 state and O state) under different process parameters. Results showed that the chemical milling rate in T8 state was higher than that in O-state under different process parameters, and the side cutting rate in T8 state was more stable than that in O-state. Meanwhile, the surface quality of 2195 Al-Li alloy after chemical milling was related to the heat treatment state. The O-state sample had different degrees of etching grooves at the rib position after chemical milling, while the T8-state sample was smooth and flat and had better surface quality after chemical milling.

Cite this article

XIAN Peng, FU Qiang, ZHENG Sen-mu, TANG Shuai, HUANG Peng-fei . Effect of Different Heat Treatment States on Chemical Milling Properties of 2195 Al-Li Alloy[J]. Materials Protection, 2023 , 56(1) : 77 -81 . DOI: 10.16577/j.issn.1001-1560.2023.0012

References

[ 1] 杜 康, 王军强, 曹海龙,等. 航空航天用铝锂合金研究进展及发展趋势[J]. 铝加工, 2022(2): 3-9.DU K,WANG J Q,CAO H L,et al. Research Progress and Development Trend of Al-Li Alloys for Aerospace Applications [J]. Aluminum Processing, 2022(2):3-9.

[ 2] 冯朝辉,于 娟,郝 敏,等. 铝锂合金研究进展及发展趋势[J]. 航空材料学报, 2020, 40(1): 1-11.FENG C H, YU J, HAO M, et al. Research Progress and Development Trend of aluminum-lithium alloys [J]. Journal of Aeronautical Materials, 2020, 40(1): 1-11.

[ 3] 沈连桂. 化学铣切[M].北京:国防工业出版社,1984.SHEN L G. Chemical milling [M]. Beijing:National Defense Industry Press, 1984.

[ 4] 刘凤娟, 陈永来, 于 峰, 等. 2195 铝锂合金的化学铣切工艺优化[J]. 机械工程材料, 2019, 43(2): 34-38.LIU F J, CHEN Y L, YU F, et al. Optimization of Chemical Milling Process for 2195 Al Li alloy [J]. Mechanical Engineering Materials, 2019, 43(2): 34-38.

[ 5] 王帅东, 张昕宇, 赵武军,等. 2195 铝锂合金碱性化学铣切工艺探究[J]. 电镀与精饰, 2020, 42(1):33-35.WANG S D, ZHANG X Y, ZHAO W J, et al. Study on the Alkaline Milling Process of 2195 Al-Li Alloy [J]. Electroplating and Finishing, 2020, 42(1): 33-35.

[ 6] MA Y L, LI J F, ZHANG R Z, et al. Strength and structure variation of 2195 Al-Li alloy caused by different deformation processes of hot extrusion and cold-rolling [J]. Journal of China Nonferrous Metals, 2020, 30 (4): 835-849.

[ 7] 魏修宇, 谭澄宇, 郑子樵, 等. 时效对2195 铝锂合金腐蚀行为的影响[J]. 中国有色金属学报, 2004, 14(7):1 195-1 200.WEI X Y,TAN C Y,ZHENG Z Q,et al. Influence of aging on corrosion behavior of 2195 Al -Li alloy [J]. Chinese Journal of Nonferrous Metals,2004,14 (7):1 195-1 200.

[ 8] FENG B, XIONG B Q. Effect of Annealing Temperature on the Microstructure of 2195 Al-Li Alloy Sheet[J]. Materials Science Forum, 2021, 1 026: 49-58.

[ 9] 毛大恒, 张 灿, 周亚军, 等. 2197 铝锂合金化学铣切工艺的探讨[J]. 材料保护, 2010, 43(10): 33-35.MAO D H, ZHANG C, ZHOU Y J, et al.Chemical Milling Process for 2197 Aluminum-Lithium Alloy [J]. Materials Protection, 2010, 43(10): 33-35.

[10] 胡丽敏, 成 桃, 李爱文, 等. 热处理对2195 铝锂合金组织及性能的影响[J]. 航天制造技术, 2021(6):22-25.HU L M, CHENG T, LI A W, et al. Effect of Heat Treatment on Microstructure and Properties of 2195 Al-Li Alloy[J]. Aerospace Manufacturing Technology, 2021 (6):22-25.
Outlines

/