Study on Corrosion Behavior of Pressure Vessel Steel in Simulated Industrial Wharf Atmospheric Environment

GAN Bang, MA Kaijun, CAO Gongwang, WANG Zhenyao

doi:10.16577/j.issn.1001-1560.2024.0005

Materials Protection >

2024 , Vol. 57 >Issue 1: 28 - 35

DOI: https://doi.org/10.16577/j.issn.1001-1560.2024.0005

Study on Corrosion Behavior of Pressure Vessel Steel in Simulated Industrial Wharf Atmospheric Environment

Expand

(1.PipeChina Network Corporation Eastern Oil Storage and Transportation Co.，Ltd.，Xuzhou 221008，China；2.Institute of Metal Research，Chinese Academy of Sciences，Shenyang 110016，China；3.Liaoning Provincial Key Laboratory of Environmental Corrosion and Evaluation of Materials，Shenyang 110016，China)

CAO Gongwang (1986-)，Senior Engineer，Master，Research Focus: Atmospheric Environment Corrosion，Tel.:15040144450，E-mail:gwcao＠imr.ac.cn

Received date: 2023-07-25

Revised date: 2023-09-10

Accepted date: 2023-09-15

Online published: 2024-01-30

Fold

Abstract

For studying the corrosion behavior of pressure vessel steel in simulated industrial marine atmospheric environment，the weight loss analysis，EDS，XRD and electrochemical methods were used to study the corrosion behavior of pressure vessel steel Q235 and 16MnNiVR under different simulated accelerated test cycles.Results showed that in the simulated industrial marine atmospheric environment，the corrosion rate of pressure vessel steel Q235 and 16MnNiVR first exhibited an upward trend.As the rust layer gradually changed from loose to dense，the corrosion rate would decrease to varying degrees.Under this accelerated test，the chemical properties of the corrosion products of the two steels were consistent，and the difference in corrosion behavior was caused by the compactness of the corrosion products on the surface of the metal substrate.Besides，the corrosion resistance of 16MnNiVR steel could reach 1.6 times of that of Q235 steel under the action of corrosion factor of industrial marine atmosphere environment in the southeast coast.

Key words： pressure vessel steel; industrial wharf atmosphere; simulated accelerated test; corrosion behavior