Effect of Volume Fraction of EAA on the Swelling Effect of PC-ABS in EAA-NMP-H2O Swelling System

Expand
  • (1. College of Chemistry and Chemical Engineering, Ningxia Normal University,Guyuan 756000, China;
    2. Key Laboratory of Green Catalytic Materials and Technologies, Ningxia Hui Autonomous Region,Guyuan 756000, China;
    3. Xi’an Aerospace City Fourth Primary School, Xi’an 710199, China;
    4. College of Information Science and Engineering, Northeastern University, Shenyang 110819, China)

ZHAO Wenxia (1978-), Professor, Ph.D., Research Focus: Surface Modification of Engineering Plastics, Electroless Plating and Electroplating, E-mail: zwxchj2006@163.com

Received date: 2023-05-29

  Revised date: 2023-07-21

  Accepted date: 2023-08-21

  Online published: 2024-04-30

Supported by

National Natural Science Foundation of China (21561027); Natural Science Foundation of Ningxia (2023AAC03340, 2023AAC03326, 2022AAC03298); Innovation and Entrepreneurship Project for Returnees of Ningxia (Ning Renshe Letter[2024] No. 4); Science and Technology Innovation Leading Talent Project of Ningxia (KJT2016004); Ningxia New University Think Tank Project ([2018] 12); Liupanshan Resources Engineering and Technology Research Center (HGZD22-18 & HGZD23-09); Key Discipline of Inorganic Chemistry ([2017] 83); Key Research Project of Ningxia Normal University (XJZDD2321)

Abstract

To investigate the effects of ethyl acetoacetate(EAA) concentration and swelling time on the swelling performance of polycarbonate-polyacrylonitrile-butadiene-styrene copolymer(PC-ABS) in swelling system, the PC-ABS substrates were subjected to swelling treatment using EAA-N-methyl-2-pyrrolidinone(NMP)-H2O system. Subsequently, employing an H2SO4-MnO2-H2O system as the micro-etching system, the PC-ABS substrates were micro-etched for 20 min at 70 ℃. Results showed that when the volume fraction of EAA in the swelling system was 50% and the swelling temperature was 55 ℃, the PC-ABS could obtain appropriate swelling degree after 5 min of swelling. Following this condition, swelling and micro-etching treatments led to the formation of evenly distributed and dense pores on the surface of the PC-ABS substrates. The contact angle between the substrate surface and water decreased, enhancing the hydrophilicity of the substrate surface. Consequently, the adhesive strength between the subsequently electroless copper plating layer and the PC-ABS substrate reached 4.03 N/cm, achieving the desired swelling and micro-etching effects.

Cite this article

HUI Kaihong, ZHAO Wenxia, LIU Xin, LI Xinwei, ZHAO Wei, SONG Yifan, LI Dongping, YAN Yani, ZHU Qian, CHEN Huaijun, HUI Kaining . Effect of Volume Fraction of EAA on the Swelling Effect of PC-ABS in EAA-NMP-H2O Swelling System[J]. Materials Protection, 2024 , 57(4) : 156 -162 . DOI: 10.16577/j.issn.1001-1560.2024.0089