Effect of Preparation Process Parameters on the Infrared Emissivity of Fluorocarbon Resin/Aluminum Powder Coatings

MA Chuang, WANG Zhen, WANG Xinyu, FENG Zenghui, WANG Xingli, LIU Lanxuan

doi:10.16577/j.issn.1001-1560.2024.0135

Materials Protection >

2024 , Vol. 57 >Issue 6: 121 - 130

DOI: https://doi.org/10.16577/j.issn.1001-1560.2024.0135

Effect of Preparation Process Parameters on the Infrared Emissivity of Fluorocarbon Resin/Aluminum Powder Coatings

Expand

(1. China Academy of Machinery Wuhan Research Institute of Materials Protection Co., Ltd., Wuhan 430030, China;2. China Ship Development and Design Center, Wuhan 430000, China)

FENG Zenghui, Researcher, Research Focus: The Corrosion and Protection of Marine Coatings and Materials, Tel.: 13419694843,E-mail: 13419694843@163.com

Received date: 2023-04-15

Revised date: 2023-04-23

Accepted date: 2023-04-28

Online published: 2024-06-24

Fold

Abstract

In order to obtain coatings with low emissivity, most studies focus on the screening of resin and filler components. However, the influence of process parameters on emissivity during the coating preparation process was rarely studied, and the interaction between various preparation processes was not analyzed. In this study, aluminum powder was selected as the metal filler and fluorocarbon resin was selected as the adhesive to prepare a low-infrared emissivity coating. Initially, single-factor experiments were conducted to regulate the viscosity of the coating(achieved by varying the amount of diluent added to the coating), the wet film thickness of the coating and the curing temperature. The combined effects of these three process parameters on the distribution of aluminum powder in the coating and the infrared emissivity of the coating were analyzed and studied. The response surface methodology was used to further analyze the interactions between the process parameters, and the optimal combination of process parameters were determined to guide the actual coating preparation process. Results showed that the influence of the three process parameters on the emissivity of the coating decreased in the order of coating viscosity > curing temperature > wet film thickness. When the addition amount of diluent was 78 g, the film thickness was 60 μm, and the curing temperature was 73 ℃, the infrared emissivity of the coating was 0.141 in the band of 3～5 μm and 0.177 in the band of 8～12 μm.

Key words： fluorocarbon resin/aluminum powder coating; low emissivity; preparation process; viscosity; film thickness; curing temperature; response surface method

Cite this article

MA Chuang, WANG Zhen, WANG Xinyu, FENG Zenghui, WANG Xingli, LIU Lanxuan . Effect of Preparation Process Parameters on the Infrared Emissivity of Fluorocarbon Resin/Aluminum Powder Coatings[J]. Materials Protection, 2024 , 57(6) : 121 -130 . DOI: 10.16577/j.issn.1001-1560.2024.0135