Effect of Ce Element on the Microstructure and Corrosion Resistance of DH36 Ship Plate Steel

Expand
  • (School of Materials and Metallurgy， Inner Mongolia University of Science and Technology， Baotou 014010， China)


YANG Jichun (1963-)， Ph.D.， Professor， Research Focus: Application of Rare Earth Elements in Steel， Tel.:13947258182， E-mail: yangjichun1963＠163.com；

LIU Xiangjun (1987-)， Ph.D.， Lecturer， Research Focus: Basic Application Research of Rare Earth Elements in Steel， Tel.: 15771250325， E-mail: liuxiangjun2014＠yeah.net

Received date: 2024-07-19

  Revised date: 2024-09-27

  Accepted date: 2024-09-29

  Online published: 2024-11-14

Supported by

National Natural Science Foundation of China Youth Project (52204364)； Basic Research Funds for Directly Affiliated Universities in Inner Mongolia Autonomous Region (2023QNJS011)；General Funding from the China Postdoctoral Science Foundation (2021MD703850)； Central Guidance for Local Scientific and Technological Development Funding Projects(2022ZY0090)

Fold

Abstract

Currently， there are fewer studies on the effect of rare earths on the corrosion resistance of DH36 ship plate steel.Herein， the effect of the addition of rare earth Ce on the microstructure and corrosion resistance of DH36 ship plate steel was studied by metallographic microscope， scanning electron microscope， electrochemical workstation and X-ray diffractometer.Results showed that Ce had a significant refining effect on the grain size of the test steel； The addition of Ce modified the Al2O3， MnS and Al2O3＋MnS inclusions in the steel to CeAlO3＋MnS，Ce2O3 inclusions，and the stress around rare earth inclusions significantly decreased，reducing the active zone where corrosion occurred.Moreover， the addition of Ce increased the self-corrosion potential of the test steel and reduced the self-corrosion current density.After immersed in 3.5%NaCl solution for 5 d， the corrosion current density of the test steel decreased from 8.431×10-5 A/cm2 without the addition of rare earth Ce to 2.384×10-5 A/cm2 with the Ce content of 0.009 2%； The addition of Ce declined the content of γ-FeOOH in the corrosion products，while increased the content of α-FeOOH and Fe3O4.All of test results indicated that the increase of Ce content would improve the corrosion resistance of the test steel.

Key words： Ce; DH36 ship plate steel; inclusion; corrosion resistance

Cite this article

ZHU Yingjie, MENG Xiangchao, LIU Xiangjun, YANG Changqiao, WANG Ting, YANG Jichun . Effect of Ce Element on the Microstructure and Corrosion Resistance of DH36 Ship Plate Steel[J]. Materials Protection, 2024 , 57(9) : 10 -19 . DOI: 10.16577/j.issn.1001-1560.2024.0196

Options
Outlines

/

〈 〉

Total visitors: 　Visitors of today: 　Now online:
Website Copyright © Editorial Department of Materials Protection
Powered by Beijing Magtech Co. Ltd,.