Analysis of the Influence of Ferromagnetic Corrosion Products on Magnetic Flux Leakage Detection of Pipeline

ZHU Xinghui, HU Peng, MENG Xiangji, LYU Tan, GUO Bin, CHEN Jinzhong, ZHOU Demin

doi:10.16577/j.issn.1001-1560.2024.0242

Materials Protection >

2024 , Vol. 57 >Issue 10: 208 - 212

DOI: https://doi.org/10.16577/j.issn.1001-1560.2024.0242

Analysis of the Influence of Ferromagnetic Corrosion Products on Magnetic Flux Leakage Detection of Pipeline

Expand

(China Special Equipment Inspection ＆ Research Institute， Technology Innovation Center of Oil And Gas Pipeline and Storage Equipment Safety for State Market Regulation， Beijing 100029， China)

LV Tan(1988-)， Engineer， Research Focus: Non-Destructive Testing Technology of Long-Distance Pipeline，Tel.: 010-59068232，E-mail: lvshaotan＠126.com

Received date: 2024-04-01

Revised date: 2024-06-10

Accepted date: 2024-06-11

Online published: 2024-12-22

Supported by

National Key R ＆ D Program of China (2022YFC3070100)

Fold

Abstract

Magnetic flux leakage internal detection is an efficient method for detecting defects in long-distance pipelines.However，some corrosion points (such as stray current corrosion) contain a large amount of ferromagnetic corrosion products， which can affect the overflow of the leakage magnetic field at the defect site， resulting in a smaller evaluation of the detected data and even missed detections.Based on the fundamental principles of magnetic flux leakage internal detection， the reasons for the generation of leakage magnetic fields at defect sites were elucidated.Combined with pull-out tests and practical engineering cases， it was demonstrated that ferromagnetic corrosion products hinder the leakage of magnetic fields at corrosion defects.This provided technical support for enhancing the identification of such defects in the future and improving the effectiveness of pipeline magnetic flux leakage internal detection.

Key words： magnetic flux leakage internal detection; ferromagnetic corrosion products; leakage magnetic field; data evaluation